CASE STUDIES

STEEL INDUSTRY ALUMINUM INDUSTRY ASSET MANAGEMENT PRODUCT COATING CERAMICS INDUSTRY CONCRETE INDUSTRY

Steel Industry

Object Steel Slab
Application Temperature 750℃
Products HP-700T
Object Steel Coil
Application Temperature 550℃
Products HP-600
Object Steel Billet
Application Temperature 750℃
Products HP-700T
Object Steel Wire
Condition Pickling ( H2SO4, HCl )
Annealing ( 800℃ x 10hours )
Products HP-M83
Object Forged steel
Condition Hot nailing at 800℃
Annealing ( 1100℃ x 18 hours )
Products HP-L90

Aluminum Industry

Object Aluminum Sow
Application Temperature 550℃
Products HP-600
Object Aluminum Billet
Application Temperature r.t~400℃
Annealing Temperature 550℃
Products HP-350N, 380N+, 360
Object Jigs for heat treatment process
Annealing (500℃ x several hours ) x cycles
Products HP-T42, HP-CBR Tag

Asset Management

Object Jigs for heat treatment
Heating condition (250℃ x several hours
x cycles
Products HP-T42, HP-CBR Tag
Object Injection Casting Mold
Heating condition (200-400℃ x several hours )
x cycles
Products HP-120S, HP-150N, HP-350N, HP-CBR CX2

Product Coating

Object Machine tools, automotive parts
Condition treatment such as cleansing,pickling or baking after coating ( 250℃ x 30min )
Products HP-PC10, HP-T40

Ceramics Industry

Object Jigs ( Alumina, Glass, Carbon )
Heating condition 1000℃ x over 10hours
Products HP-CBR CX2, HP-CBR HB
Object Crucible
Heating condition 1000℃ x several hours
Products HP-CBR CX2, HP-CBR HB

Concrete Industry

Object Cement pipe or blocks
Condition Autoclave process
10atm 180-200℃ x over10 hours
Products HP-120SH4